15crmo wonn asye (GB/T 3077) gen yon konpozisyon nan 0.12-0.18% kabòn (C), 0.40-0.70% Silisyòm (SI), 0.40-0.70% Manganèz (MN), 0.80-1.10% CHROMIUM (CR), 0.40-0.55% MOLEMENTHEN MELEMENTHENTHENTHENTHENS OSWA PWOJÈ ( egal a 0.035% S.
Konpare ak 12cr1mov (0.08-0.15% C, 0.17-0.37% SI, 0.40-0.70% MN, 0.90-1.20% CR, 0.25-0.35% MO, 0.15-0.30% V), 15crmo gen de diferans chimik ki pa gen okenn modere {
Pi wo molibden (0.40-0.55% vs . 0.25 - 0.35%): Plis Mo amelyore rezistans fluaj nan tanperati modere pa ralanti difizyon atomik - difizyon se kòz prensipal la nan ranpe (deformation dousman). MO tou fòme ki estab mo₂c carbides ki reziste coarsening nan 350-500 degre, kenbe kapasite yo nan PIN debwatman.
Pa gen vanadyòm: Vanadyòm 12cr1mov a (0.15-0.30%) fòme carbides VC ki trè efikas nan tanperati ki wo (500-550 degre) men nesesè nan tanperati modere. San V, 15crmo gen yon estrikti carbure ki pi senp (CR₂₃C₆, Mo₂c) ki se pi estab ak mwens tendans yap divòse nan 350-500 degre.
Pi wo kabòn (0.12-0.18% vs . 0.08 - 0.15%) nan 15crmo bay plis C pou fòmasyon carbure, ogmante fòs nan tanperati modere san yo pa risk yo fragilite ki asosye ak pi wo C nan segondè - asye tanperati. Silisyòm (0.40-0.70%) se pi wo pase 12cr1mov a, amelyore rezistans oksidasyon nan tanperati modere pa epesman kouch nan SiO₂ anba cr₂o₃.