310S asye pur wonn (ASTM A276; GB 06CR25NI20) gen yon segondè - konpozisyon alyaj: 24.0-26.0% CHROMIUM (CR), 19.0-22.0% NICKEL (NI), mwens pase oswa egal a 0.08% (C), mwens pase oswa egal oswa egal oswa egal oswa egal (mwens pase oswa egal (mwens pase oswa egal oswa egal (mwens pase oswa egal (mwens pase oswa egal (mwens pase oswa egal (mwens pase oswa egal (mwens pase oswa egal (mwens pase oswa egal (mwens pase oswa egal (mwens pase oswa egal (mwens pase. Manganèz (MN), mwens pase oswa egal a 0.045% P, mwens pase oswa egal a 0.030% S.
Konpare ak 304 (18-20% Cr, 8-10.5% Ni), 310s gen byen lwen pi wo Cr ak Ni kontni - sa yo se chofè yo prensipal nan rezistans chalè li yo.
Chimikman, 310s reziste tanperati ki wo (jiska 1150 degre) atravè de mekanism:
Kouch oksid CHROMIUM: pi wo CR (24-26%) fòme yon pi epè, plis ki estab kouch pasif pase 304. Kouch sa a reziste oksidasyon (reyaksyon ak oksijèn) ak sulfidasyon (reyaksyon ak souf) nan tanperati ki wo - kòz komen nan degradasyon nan founo endistriyèl yo.
Nikèl - Austenit estabilize: pi wo Ni (19-22%) konplètman estabilize mikrostruktur austenitik (FCC), anpeche fòmasyon nan faz sigma frajil (yon Cr - ni konpoze intermetallic) nan 600-800 degre. Fòmasyon faz Sigma nan pi ba - Ni klas (tankou 304) lakòz embrittlement ak diminye rezistans chalè.
Ba kabòn (mwens pase oswa egal a 0.08%) minimize fòmasyon carbure nan limit grenn jaden, ki ta febli asye a nan tanperati ki wo, pandan y ap SI/MN èd nan deoxidation san yo pa konpwomèt rezistans chalè.