440C asye pur wonn (ASTM A276; GB 10CR17MO) gen yon konpozisyon: 0.95-1.20% kabòn (C), 16.0-18.0% CHROMIUM (CR), 0.75-1.25% MOLYBDENUM (MO), mwens pase oswa egal a 1.00% SILICON (SI), SILIK (SILI), MOLYBDENN (MO), OWERS), OSWA), OSWA), OSWA), OSWA), OSWA), OSWA), OSWA), OSWA), OSWA), OSWA), OSWA), OSWA (SILI OSWA). 0.040% P, mwens pase oswa egal a 0.030% S.
440A diferan nan de fason kle: pi ba kabòn (0.60-0.75% C) e pa gen okenn entansyonèl molibdèn (Mo mwens pase oswa egal a 0.50%).
Diferans sa yo fè 440C siyifikativman pi rèd akòz mekanis chimik:
Pi wo kabòn: 0.95-1.20% C ogmante fòmasyon nan karbid CHROMIUM (CR₇C₃, CR₂₃C₆) pandan tretman chalè. Carbides yo difisil, patikil frajil ki embed nan matris la martensitic, ogmante an jeneral dite-440C gen ~ 50% plis carbides pase 440A.
Te ajoute molibdèn: 0.75-1.25% mo fòm molibdèn carbides (Mo₂c) ki pi rèd pase karbid CHROMIUM. Mo tou amelyore hardenability, asire karsid fòme egzakteman menm jan nan tout asye a (pa sèlman nan sifas la), ki amelyore konsistans dite.
CHROMIUM (16-18%) bay rezistans korozyon men tou kontribye nan dite via fòmasyon carbure. San yo pa Mo ak pi ba C, 440A fòme mwens, douser carbides, sa ki lakòz pi ba dite (56-58 HRC vs . 58 - 60 HRC pou 440C).