15CrMn round steel (GB/T 3077) has a composition of 0.12–0.18% carbon (C), 0.17–0.37% silicon (Si), 1.10–1.40% manganese (Mn), 0.80–1.10% chromium (Cr),<=0.035% P,<=0.035% S.
Konpare ak asye 15cr (0.12-0.18% C, 0.17-0.37% SI, 0.30-0.60% MN, 0.80-1.10% CR), Manganèz (1.10-1.40%) amelyore duktilite via de mekanism chimik:
Rediksyon nan faz frajil: MN reyaji ak souf yo fòme ductile sulfid Manganèz (MNs) olye pou yo sulfid fè frajil (FES). Nan 15cr asye, Fes segregasyon nan limit grenn jaden ak lakòz "cho kout" (fragilite pandan k ap travay cho). MNS se pi plis ki estab ak gaye egzakteman menm jan, elimine feblès fwontyè ak ogmante elongasyon pa 30-40% (ki soti nan ~ 18% nan 15cr a ~ 25% nan 15crmn).
Austenit estabilizasyon pandan refwadisman: Mn reta transfòmasyon nan austenit ferit/pearlite pandan refwadisman, sa ki pèmèt plis tan pou fòmasyon nan amann - grenn fen. Grenn amann gen plis limit pou absòbe enèji pandan deformation, plis amelyore duktilite san sakrifye fòs.
CHROMIUM bay fòs baz pa fòme carbides, men MN asire fòs sa a pa vini nan pri a nan duktilite - fè 15crmn byen lwen plis fòmab pase 15cr.