20crni3a asye wonn (GB/T 3077) gen yon konpozisyon nan 0.17-0.23% kabòn (C), 0.17-0.37% Silisyòm (SI), 0.30-0.60% Manganèz (MN), OWCHELN OWCHELN (OWCHEL (30-0.90% OWN (OWN (OWN (OWN (OWN (OWN (OWN (OWN (OWN (OWN (OWN (OWN (OWN (OWN (OWN (OWN (OWN (OWN (OWN (OWN (OWN (OWN (OWN NOM, OWN NOM, OWN (OWCEL OWCHEL (30.90% (OWN PWOGRAM OWCELACH OWCELACH (3. 0.030% S.
Nikèl (2.70–3.20%) se eleman prensipal ki amelyore ba - tanperati a, aji nan de mekanism chimik:
Ductile - Tanperati tranzisyon frajil (DBTT) Bese: Pifò asye ferritik sibi yon ductile - tranzisyon frajil - vin frajil anba yon sèten tanperati. Nikèl diminye DBTT a nan 20crni3a a - 60 degre oswa pi ba, konpare ak -20 degre pou ba -Ni asye (egzanp, 20cr ak<0.5% Ni). This is because Ni atoms disrupt the formation of brittle martensite at low temperatures, keeping the steel ductile.
Ranfòse fwontyè grenn jaden: nikèl segregasyon nan limit grenn jaden, diminye segregasyon an nan enpurte danjere tankou fosfò. P gen tandans nan gwoup nan limit yo ak febli yo nan tanperati ki ba, men Ni mare ak P yo fòme konpoze ki estab, anpeche fwontyè embrittlement.
CHROMIUM (0.60-0.90%) bay fòs pa fòme carbides, pandan y ap ba kabòn (0.17-0.23%) minimize fòmasyon carbure frajil - tou de sipòte nikèl a ki ba - efè severite tanperati.